40CrMo 偏析碳化物?

leomet · 发表于 2009-11-15 07:20:25

本帖最后由 leomet 于 2015-5-14 19:04 编辑

More photos from this faulty steel axle that cracked during induction hardening.

後來覺得這些的確不是碳化物.

790512as · 发表于 2009-11-15 10:37:05

吴老师是个经验丰富的前辈，但上面的白色组织我个人认为不是碳化物，碳化物与碳含量有关，这种材料不可能出现这么多碳化物，是不是碳化物可以在倍数高的显微硬度计上检测一下硬度就知道了

leomet · 发表于 2009-11-16 08:08:41

To all:
Is there proeutectoid carbide in this normalized 45# steel?
It says in textbook that proeutectoid product in 45# steel is Ferrite.

leomet · 发表于 2009-11-16 08:20:49

The above micrographes are from the axles shown below.
These axles for lathe showed microcracks after induction hardening. Some showed microcracks after tempering. 本帖最后由 leomet 于 2009-11-16 08:22 编辑

lydia · 发表于 2009-11-18 14:46:13

17# lydia
蝕坑 etch pit.
leomet 发表于 2009-11-14 08:00

谢谢您。

那么再请问一下那个蚀坑是怎么产生的？轧制材料和锻材一般看不到，我只在堆焊材料上看到过。

leomet · 发表于 2009-11-18 21:06:57

22# 790512as
On my second thought, I think you are correct about this. I should change my view point on this, some how. Thanks for reminding me.
Those white spots might be over-saturated austenite. But some carbide particles are among them is for sure. It is these
carbide particle ( in bad shapes) that give induction heattreaters headaches. 本帖最后由 leomet 于 2009-11-19 06:42 编辑

天山雪莲 · 发表于 2009-11-19 13:53:11

可以分析一下，42CrMo在什么情况下会有碳化物：
42CrMo属亚共析钢，无论是在那种状态下都很难出现游离态的碳化物。

888888 · 发表于 2009-11-21 12:59:00

此图片不像液析,液析不会沿晶界成网状分布,而多是沿变形方向且量少无多边形形态

ZMQ · 发表于 2010-1-8 14:14:45

是铁素体吧】

vedbox · 发表于 2010-7-29 13:37:51

下班回来再学习下。

韩文 · 发表于 2010-7-29 15:15:02

看着不像碳化物。你可以做一下电镜。打一下成分不就知道了

青青园中葵 · 发表于 2015-5-15 10:45:48

好崇拜业界前辈！什么时候才能学到这个程度？