其实并非十分清楚---关于“索氏体”

搬运工

njxwl 发表于 2012-4-27 08:08
Sorbite was named in honor of the English scientist H. C. Sorby (1826–1908). It is formed as a resu ...

你好。
谢谢关注。
   将你上传的资料分成两段内容；
    1。Sorbite ：
   Sorbite was named in honor of the English scientist H. C. Sorby (1826–1908). It is formed as a result of the decomposition of austenite at a temperature of approximately 650°C. The distance between the lamellae in sorbite is 0.2 micrometer, whereas in pearlite it is 0.5–1.0 micrometer. The hardness, strength, and impact strength of sorbite are greater than those of pearlite.
   2。 Tempered sorbite;
   The ferrite-carbide mixture formed as a result of hardening and high-temperature tempering is sometimes called tempered sorbite.
  烦请提供资料出处？
  另，你如何看待20楼的回复。。。。

xyz123zhao

看来理不辨不明啊，索氏体这个我还真不清楚，只按照GB13320上进行对比的
  谢谢各位

njxwl

“索氏体是一种不稳定组织，在铁碳平衡图上找不到的”，我不敢苟同，索氏体实际就是细珠光体，而珠光体在相图上是有的，至于“球状索氏体”没听说过，应该是淬火+高温回火得到的回火索氏体，是在铁素体基体上分布粒状渗碳体组织。
搞清这些组织名词来意，对于我们理解热处理相关知识是有好处的。
组织决定性能，为何调质性能好于正火性能，可以从组织上得到解释

冰剑

索氏体是一种不稳定组织，在铁碳平衡图上找不到的，可用正火，和等温转变获得片状索氏体，也可以用450-600回火的到球状索氏体。总体来说淬火+高温回火得到的索氏体机械性能能优于前者，这就是为什么我们经常多用调质得到索氏体的原因，正火后的机械性能，和调质后的机械性能，很多资料都有对比。至于为什么叫索氏体，我觉得大家没必要去深究。只要了解其在此状态下的性能就可以了。

njxwl

资料出处：http://encyclopedia2.thefreedictionary.com/Sorbite

njxwl

关于20楼回复，总体来说正确，但珠光体、索氏体和屈氏体为层片状结构，，不同的是片间距不同，而贝氏体的结构与上述三者还是有很大区别的