美国图纸1/4硬刚是什么意思
有些老外的图纸上注明有1/4、1/2硬是什么意思？ 不是很清楚,是不是半马区在1/4或1/2呀 也可能是是淬透性中至淬火端的距离，老外用英寸表示的。那么1/4硬应是至淬火端1/4英寸处的硬度 麻烦楼主能把出现1/2、1/4的时候周围的文字一并打出来，方便分析，若可能最好将图纸扫描。回复 1# 的帖子
上網抓的:Temper(質別) Data
Stainless Strip Steel (Cold Rolled) - Temper Classifications -
Note(註) - The various stainless strip tempers are based on specified minimum values for tensile strength or yield strength or both. Here at Precision Steel there is on file a complete record of all such detail including chemical analysis on each item in stock. However, because of custom, both distributors and customers alike rely on approximate Rockwell readings for temper classification. To illustrate:
TemperRockwell Tensile PSI
Soft Approx. B 87 max 75.000 min.
Quarter hard Approx. C 25/30 125.000 min.
Half Hard Approx. C 30/35 150.000 min.
Three Quarter hard Approx. C 35/40 175.000 Min.
Full Hard Approx. C 40/45 185.000 Min.
Extra Hard (Tyoe 301) Approx. C 45 min. 200.000 Min.
Type 430 Soft Approx. B 75/85 75/85.000
[ 本帖最后由 leomet 于 2008-6-3 21:17 编辑 ] 很想知道这是什么意思,好长点见识.有那位知道的,请解释一下,谢谢 加热数据
不锈钢带钢（冷轧） -磨炼分类-
注意-各种不锈钢带加热是基于特定的最低值，拉伸强度或屈服强度，或两者均有。在这里有对每个项目的精密钢有关于档案的完整记录所有这些细节包括化学分析。不过，由于自订，无论是分销商和客户都依赖于近似罗克韦尔读为磨炼分类。
说明： 请看ASTM标准：A666 ,里面有对不锈钢冷轧钢带，不同冷作硬化钢带力学性能的规定！
[ 本帖最后由 webwonder 于 2008-6-3 14:35 编辑 ]
回复 7# 的帖子
Temper 用於人: 脾氣 氣質; 用於材料: 質別用於淬火後: 回火
回复 9# 的帖子
您直接把原文译出来不更好吗，论坛内真正精通英语的恐怕不太多，哈，包括我本人。 应该这么解释吧！扎制板材或型材会产生硬化，若交货时不进行退火处理即为全硬，通过退火处理硬度依次下降为1/2硬，1/4硬，1/8硬和退火硬度
[ 本帖最后由 wangweiccgc 于 2008-6-7 15:39 编辑 ] 可能是基于不锈钢来标的.
不同种类的不锈钢的硬度值是不一样的(即使同样的1/4H、1/2H等）
牌号 硬度 屈服强度（N/MM2） 抗拉强度（N/MM2） 硬度（HV）
SUS301 SOFT 205min 520min 218max
1/4H 510min 860min 250-310
1/2H 755min 1030min 310-370
3/4H 930min 1210min 370-430
H 960min 1270min 430-490
EH 1275min 1569min 490min
SUS304 SOFT 205min 520min 200max
1/4H 345min 690min 200-250
1/2H 410min 760min 250-310
3/4H 480min 820min 310-370
H 685min 930min 370-430 不仅仅是不锈钢，其他材料也都有，主要根据硬度来区分，相当于一种材料硬度状态，软态、1/8硬化态，1/4硬化态。。。 GB标准里也有类似说法。有色金属（比如铜合金）的材质标准，会用到1/4硬，1/2硬......概念。可参考GB/T 21652。