碳势控制
欧陆(eurotherm)仪表在碳势控制上的应用气体渗碳是http://images.gkcity.com/Attachment/Image/GeneralKey/weile.gif增加钢件表层http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif含碳量和一定http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif碳浓度梯度，将钢件http://images.gkcity.com/Attachment/Image/GeneralKey/zai.gif渗碳介质中加热并保温使碳原子渗入钢件表层http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif化学热处理工艺称为渗碳。渗碳是使碳原子渗入钢制工件表层http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif化学热处理工艺。渗碳后，工件表面含碳量一般高于0.8%。淬火并低温回火后，http://images.gkcity.com/Attachment/Image/GeneralKey/zai.gif提高硬度和耐磨性http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif同时，心部能保持相当高http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif韧性，可承受冲击载荷，疲劳强度较高。碳工艺广泛应用于飞机、汽车、机床等设备http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif重要零件中，如齿轮、轴和凸轮轴等。渗碳是应用最广、发展http://images.gkcity.com/Attachment/Image/GeneralKey/de2.gif最全面http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif化学热处理工艺。
欧陆仪表内部带有氧化锆探头计算功能模块。可以用来测量碳势，炉气露点或炉气中氧气浓度。氧化锆探头产生一个mV级信号。该信号http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif大小取决于炉外http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif探头参考侧气体中氧气http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif浓度与炉内气氛中氧气http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif浓度之间http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif比率。控制器利用温度和碳势信号计算出炉内气氛http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif实际碳势。碳势回路通常具有两个输出通道，一个输出用来控制向炉内添加富碳气体http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif阀门，另一个输出用于控制稀释气体http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif多少。
下面http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif例子中，探头http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif温度传感器类型为K型热电偶，连接到模块3上。mV信号输入到模块6。
控制回路1控制温度，控制回路2控制碳势。报警输出链接到继电器AA上，为On/Off输出。
这是一个包括温度和碳势控制http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif双回路控制系统。
温度控制回路：
温度回路http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif主PV输入是K型热电偶。温度回路http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif控制输出是4-20mA连接module 5A。
碳势控制回路：
氧探头PV连接到module 6 测量mV(oxygen)，module 3 连接氧探头http://images.gkcity.com/Attachment/Image/GeneralKey/de.gifTC输入。这两个信号http://images.gkcity.com/Attachment/Image/GeneralKey/tongguo.gif软连线同时连接到碳势控制功能块。控制器利用温度和碳势信号计算出炉内气氛http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif实际碳势。控制输出分别是富气连接到1A，稀释气体连接到1C。积碳报警可http://images.gkcity.com/Attachment/Image/GeneralKey/zai.gif炉内碳浓度太高，http://images.gkcity.com/Attachment/Image/GeneralKey/yizhi.gif于http://images.gkcity.com/Attachment/Image/GeneralKey/zai.gif炉壁积碳时触发积碳报警。http://images.gkcity.com/Attachment/Image/GeneralKey/tongguo.gif编程自动清洗或http://images.gkcity.com/Attachment/Image/GeneralKey/tongguo.gif手动请求IO1去实现。通常用短促http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif压缩气体来清除探头上http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif积碳或其他沉积物。当清洗完成后，探头需要一定http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif时间才能恢复到正常测量。http://images.gkcity.com/Attachment/Image/GeneralKey/ruguo.gif恢复http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif时间太长，说明探头已老化，需要更换。http://images.gkcity.com/Attachment/Image/GeneralKey/zai.gif探头清洗和恢复http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif时间段内，碳势http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif输出保持不变（冻结），以保证炉子http://images.gkcity.com/Attachment/Image/GeneralKey/de.gif连续工作。 欧陆3504做碳控,P,I,D应该设为多少?????? 原帖由 zhm 于 2008-11-17 12:53 发表 http://www.rclbbs.com/images/common/back.gif
欧陆3504做碳控,P,I,D应该设为多少??????
你自整定或者根据控制的情况调节。不同设备PID参数肯定不同
3504碳势控制PID参数
本人调试过多个3504的碳势控制，主要有两个方面的因数： 1：氧碳头型号，如果选择MMI氧碳头需要设定一个 Process Factor， 20% CO通常为1492：PID参数， 可以选择自整定，不过需要修改P的单位为Percent，以及输出的最高限值。 有任何问题请与我联系，MB：13564710118 Henry Cui 我司使用的碳控仪,在设定碳势为0.6的状态下,碳势在0.6时会自动加富化气,本人认为应该在碳势小于0.6时才能自动加富化气,大于0.6时加空气,请问是否是碳控仪的设定有误? 不知你用的何种仪表?你说的是正常现象,为PID控制方式 原帖由 zHANG_999567 于 2008-12-10 14:57 发表 http://www.rclbbs.com/images/common/back.gif我司使用的碳控仪,在设定碳势为0.6的状态下,碳势在0.6时会自动加富化气,本人认为应该在碳势小于0.6时才能自动加富化气,大于0.6时加空气,请问是否是碳控仪的设定有误?
这是正常的!
用温度控制打个比方:当设定为600度,而pv也达到了600度.这时加热装置还是在通电一样.
通电是为了补充散失所带来的温度损失而维持这个温度.
同样的,碳势达到了设定值后也要通富化气来补偿工件渗碳等损失的碳原子. 原帖由 circle0515 于 2008-11-30 00:25 发表 http://www.rclbbs.com/images/common/back.gif
本人调试过多个3504的碳势控制，主要有两个方面的因数： 1：氧碳头型号，如果选择MMI氧碳头需要设定一个 Process Factor， 20% CO通常为1492：PID参数， 可以选择自整定，不过需要修改P的单位为Percent，以及输出的 ... 我们设置的Process Factor是56 3504的控制温度,做曲线控制保温地址怎么会是0?