求助SA-106C的C曲线，AC3,AC1,MS,MF点温度
SA-106C成分C:0.23-0.25Si≧0.1Mn:0.82-1.35 Ni≦0.30Mo≦0.1 Cr:0.40 Cu≦0.25的C曲线，AC3,AC1,MS,MF点温度！谢谢 各钢种AC1和AC3根据化学成份的计算公式
最好的办法是查阅“钢的临界温度参数手册”一类资料，我们的前辈已经为我们做了大量实验工作，常用钢数椐还是比较齐全的，而且可靠。
借花献佛，转载如下
Useful Equations For Hardenable Alloy Steels
Ae1 (°F) 1333 - 25 x Mn + 40 x Si + 42 xCr - 26 x Ni
Ae3 (°F) 1570 - 323 x C - 25 x Mn + 80 xSi - 3 x Cr - 32 x Ni
Ac1 (°C) 723 -10.7 x Mn + 29.1 x Si+16.9 x Cr -16.9 x Ni + 290 x As + 6.38 x W
Ac3 (°C) 910 - 203 x sqr(C) + 44.7 x Si- 15.2 x Ni + 31.5 x Mo + 104 x V + 13.1 x W
Ms (°F) 930 - 600 x C - 60 xMn - 20 x Si - 50 x Cr - 30 x Ni - 20 x Mo - 20 x W
M10 (°F) Ms - 18
M50 (°F) Ms - 85
M90 (°F) Ms - 185
Mf (°F) Ms - 387
Bs (°F) 1526 -486 x C - 162 x Mn - 126 x Cr - 67 x Ni - 149 x Mo
B50 (°F) Bs - 108
Bf (°F) Bs -216
Carburized Case Depth (in.) ~ .025 sqr(t), for 1700°F
Carburized Case Depth (in.) ~ .021 sqr(t), for 1650°F
Carburized Case Depth (in.) ~ .018 sqr(t), for 1600°F
(t = time in hours)
转换式
℃=5（°F－32）/ 9
针对亚共析钢：
Ac1（℃）=723-20.7Mn-16.9Ni+29.1Si+16.9Cr+290As+6.38W 偏差值：11.5℃
Ac3（℃）=910-203sqr(C) + 44.7 Si - 15.2Ni + 31.5Mo +104V + 13.1W 偏差值：16.7℃
Ms （℃）=539 - 423C - 30.4Mn- 20Si - 12.1Cr -17.7Ni - 7.5Mo 偏差值：25℃
M10=Ms-10℃ （±3℃）
M50=Ms-47℃ （±9℃）
M90=Ms-103℃ （±12℃）
Mf=Ms-215℃ （±25℃）
Bs （℃）=830 - 270C - 90Mn -70Cr -37Ni - 83Mo 偏差值：25℃
B50=Bs-60℃ （±25℃）
Bf=Bs-120℃ （±25℃）
Ac3=910-203C0.5-13.2Ni+44.7Si+104V+31.5Mo+13.1W Ac1=723-10.7Mn-16.9Ni+29.1Si+16.9Cr+290As+6.38W
常用钢种的临界温度
钢号临界温度（近似值），（oC）
Ac1Ac3Ar3Ar1Ms
优质碳素结构钢08F，0810152025303540455060708515Mn20Mn30Mn4050Mn普通低合金结构钢16Mn09Mn2V15MnTi15MnV18MnMoNb合金结构钢20Mn230Mn240Mn245Mn225Mn2V42Mn2V35SiMn50SiMn20Cr30Cr40Cr45Cr50Cr20CrV40Cr 732724735735735732724724724725727730725735735734726720 736736734700~720736 725718713715—725750710766740743721721768755 874876863855840813802790780760766743737863854812790760 849~867849~867865830~850850 840804766770840770830797838815782771771840790 854850840835824796774760751721743727695840835796768— ——779780756 740727704720———703799—730693693704745 680682685680680667680680682690690693—685682675689660 ——615635646 610627627640——645636702670693660660782700 380 220 400 340320 330330305 355 250 218
38CrSi20CrMn30CrMnSi18CrMnTi30CrMnTi35CrMo40CrMnMo38CrMoAl20CrNi40CrNi12CrNi312Cr2Ni420Cr2Ni440CrNiMo20Mn2B20MnTiB20MnVB45B40MnB40MnVB弹簧钢65708565Mn60Si2Mn50CrMn50CrVA55SiMnMoVNb滚动轴承钢GCr9GCr15GCr15SiMn763765760740765755735800733731715720720732730720720725735730 727730723726755750752744 730745770810838830825790800780940804769830780780774853843840770780774 752743737765810775788775 887—872755798705730740750——790702—660660—736795770720700681 730727695741770—746656 721——680700670650660695680730666660670575575—613625635690650639 696693—689700—688550 690700708 271 220270305250270
比较原始的计算公式（选自于--热处理工艺编制方法）：
AC3=908-2.237C+0.4385P+0.3049Si+0.3792V-0.3443Mn-0.23Ni+2(C-54+0.06Ni)
除了P外，其余元素的质量百分比数要乘以100.
求学者 发表于 2014-12-4 15:10
各钢种AC1和AC3根据化学成份的计算公式
最好的办法是查阅“钢的临界温度参数手册”一类资料，我们的前 ...
姐姐诶，这个公式在哪里搞的，给我也发一份吧！:)