有谁知道20MoCr4是什么钢材，有什么特性？十分感谢！Steel 20MOCR4 (Mat.No. 1.7321, DIN 20MoCr4, AISI 8620)
Designation by Standards
Brand Name Ravne No. Mat. No. DIN EN AISI
20MOCR4 763 1.7321 20MoCr4 20MoCr4KD 8620
Chemical Composition (in weight %)
C Si Mn Cr Mo Ni V W Others
0.20 max. 0.40 0.85 0.45 0.45 - - - -
Description
One of the most popular and widely used carborizing steels available. 20MoCr4 is a hardenable chromium, molybdenum, nickel low alloy steel often used for carburizing to develop a case-hardened part. This case-hardening will result in good wear characteristics.
Applications
Gears, shafts and other applications where a hard carborized case and a tough core are desired.
Physical properties (avarage values) at ambient temperature
Modulus of elasticity : 210
Density : 7.85
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC 20-200oC 20-300oC 20-400oC 20-500oC
11.1 12.1 12.7 12.9 13.5
Soft Annealing
Heat to 650-700oC, cool slowly. This will produce a maximum Brinell hardness of 207.
Heat Treatment
Treatment Temperature Cooling
Case hardening 880-980oC Oil (water), hot bath 160-250oC
Carburising 880-980oC Oil (water), hot bath 160-250oC
Direct hardening 860-900oC Oil, hot bath 160-250oC
Core refining 860-900oC Oil, hot bath 160-250oC
Core refining 780-820oC Oil, hot bath 160-250oC
Tempering 150-200oC Air
Hardenability Diagram
Click the image to enlarge the diagram.
Forging
Hot forming temperature: 1050-850oC.
Machinability
Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment - after carburizing machining is usually limited to grinding.
Welding
The alloy may be welded by conventional methods, usually gas or arc welding. Preheating at 200oC is beneficial and subsequent heating after welding is recommended - consult the approved weld procedure for the method used.
Cold working
The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.
Forms manufactured: Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other puposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Unless otherwise specified, registered trademarks are property of Metal Ravne company. Copyright 2011 by Metal Ravne. All rights reserved. Contact our Sales Office for more information. http://www.metalravne.com/selector/steels/20MOCR4.html 虽然全是英文，看着吃力但还是谢谢二位！ 晕，写的看不懂，就直接告诉他是和20CrMo接近不就得了吗